Structural and optical properties of sol-gel deposited proton conducting Ta{sub 2}O{sub 5} films

Conference · Tue Aug 01 04:00:00 EDT 1995

OSTI ID:205043

Ozer, N; Lampert, C M

Proton conducting tantalum oxide films were deposited by spin coating using a sol-gel process. The coating solutions were prepared using Ta(OC{sub 2}H{sub 5}){sub 5} as a precursor. X-ray diffraction studies determined that the sol-gel films, heat treated at temperatures below 400 C, were amorphous. Films heat treated at higher temperatures were crystalline Ta{sub 2}O{sub 5}. The solar transmission values (T{sub s}) of tantala films on glass generally range from 0.8--0.9 depending on thickness. The refractive index and the extinction coefficient were evaluated from transmittance characteristics in the UV-VIS-NIR regions. The refractive index values calculated at 550 nm increased from 1.78 to 1.97 with increasing heat treatment from 150 to 450 C. The films heat treated at different temperatures showed low absorption with extinction coefficients of less than k=1x10{sup -3} in the visible range. Spectrophotometric and impedance spectroscopic investigations performed on Ta{sub 2}O{sub 5} films revealed that these films have protonic conductivity of 3.2x10{sup -6} S/cm. The films are suitable for proton conducting layers in electrochromic (EC) devices.

• Research Organization: Lawrence Berkeley Lab., CA (United States)
• Sponsoring Organization: USDOE, Washington, DC (United States)
• DOE Contract Number: AC03-76SF00098
• OSTI ID: 205043
• Report Number(s): LBL--37800; CONF-9509289--1; ON: DE96004749
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ELECTRICAL PROPERTIES
ELECTROCHROMISM
FILMS
OPTICAL PROPERTIES
TANTALUM OXIDES