Effect of sulfur and magnesium on hot ductility and pitting corrosion for Inconel 690 alloy
- Chinese Academy of Sciences, Shenyang (China)
A series of hot tensile tests has been performed to study the effect of sulfur and magnesium on hot ductility of Inconel 690 alloy. The hot ductility has been evaluated from the reduction of area in hot tensile tests using a Gleeble testing machine. The value of reduction in area decreased with increasing sulfur content in the temperature range from 900 C to 1,200 C. When sulfur content was larger than 0.0025%, a ductility dip appeared, and the greater the sulfur content, the deeper and wider the ductility dip. The Scanning Electron Microscope (SEM) analyses showed that the fracture appearances changed gradually from transgranular to intergranular with increasing sulfur content, meanwhile sulfur and titanium segregation were observed at grain boundaries. The ductility dip of 690 alloy with relatively higher sulfur content could be inhibited by adding appropriate amount of magnesium. However, excessive addition led to magnesium precipitation, which was detrimental to hot ductility. The pitting test has also been conducted and the results showed that pitting rate obviously increased with increasing sulfur content.
- OSTI ID:
- 203829
- Report Number(s):
- CONF-950816-; ISBN 1-877914-95-9; TRN: 96:009795
- Resource Relation:
- Conference: 7. international symposium on environmental degradation of materials in nuclear power plants: water reactors, Breckenridge, CO (United States), 6-10 Aug 1995; Other Information: PBD: 1995; Related Information: Is Part Of Seventh international symposium on environmental degradation of materials in nuclear power systems -- Water reactors: Proceedings and symposium discussions. Volume 1; Airey, G.; Andresen, P.; Brown, J. [eds.] [and others]; PB: 664 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Ductility dip cracking susceptibility of Inconel Filler Metal 52 and Inconel Alloy 690
INCONEL 690 CORROSION IN WTP (WASTE TREATMENT PLANT) HLW (HIGH LEVEL WASTE) GLASS MELTS RICH IN ALUMINUM & BISMUTH & CHROMIUM OR ALUMINUM/SODIUM