Role of vacancies and solute atoms on grain boundary sliding
It is necessary for grain boundary dislocations to slide and climb during the grain boundary sliding process that dominates fine-grained superplastic deformation. The process of climb requires either an influx of vacancies to the grain boundary plane or a local generation of vacancies. Transmission electron microscopy (TEM) observations of grain boundaries in superplastically deformed Al-Mg-Mn alloys quenched under load from the deformation temperature have revealed the presence of nano-scale cavities resulting from a localized supersaturation of vacancies at the grain boundary. Compositional measurements along interfaces have also shown an effect of solute atoms on the local structure. This is shown to result from a coupling of vacancy and solute atom flows during deformation and quenching. Calculations of the localized vacancy concentration indicate that the supersaturation along the grain boundary can be as much as a factor of ten. The effects of the local supersaturation and solute atom movement on deformation rates and cavity nucleation and growth is discussed.
- Research Organization:
- Pacific Northwest National Lab., Richland, WA (US)
- Sponsoring Organization:
- US Department of Energy
- DOE Contract Number:
- AC06-76RL01830
- OSTI ID:
- 20104672
- Country of Publication:
- United States
- Language:
- English
Similar Records
Evidence for excess vacancies at sliding grain boundaries during superplastic deformation
Interaction of slip with grain boundary and its role in cavity nucleation