Mg segregation, difficulties of p-doping in GaN
Conference
·
OSTI ID:20104585
Transmission electron microscopy has been used to study defects formed in Mg-doped GaN crystals. Three types of crystals have been studied: bulk crystals grown by a high pressure and high temperature process with Mg added to the Ga solution and two types of crystals grown by metal-organic chemical vapor deposition (MOCVD) where Mg was either delta-doped or continuously doped. Spontaneous ordering was observed in bulk crystals. The ordering consists of Mg rich planar defects on basal planes separated by 10.4 nm and occurs only for growth in the N to Ga polar direction (000{bar 1} N polarity). These planar defects exhibit the characteristics of stacking faults with a shift vector of a 1/3 [1{bar 1}00] + c/2 but some other features identify these defects as inversion domains. Different type of defects were formed on the opposite site of the crystal (Ga to N polar direction), where the growth rate is also an order of magnitude faster compared to the growth with N-polarity. These defects are three-dimensional: pyramidal and rectangular, empty inside with Mg segregation on internal surfaces. The same types of defects seen for the two growth polarities in the bulk crystals were also observed in the MOCVD grown GaN samples with Mg delta doping, but were not observed in the crystals where Mg was added continuously.
- Research Organization:
- Lawrence Berkeley National Lab., CA (US)
- OSTI ID:
- 20104585
- Country of Publication:
- United States
- Language:
- English
Similar Records
Influence of Mg and In on defect formation in GaN; bulk and MOCVD grown samples
Mg-doped GaN: Similar defects in bulk crystals and layers grown on Al{sub 2}O{sub 3} by metal-organic chemical-vapor deposition
Influence of dopants on defect formation in GaN
Conference
·
Tue Nov 21 23:00:00 EST 2000
·
OSTI ID:771943
Mg-doped GaN: Similar defects in bulk crystals and layers grown on Al{sub 2}O{sub 3} by metal-organic chemical-vapor deposition
Journal Article
·
Sun Dec 26 23:00:00 EST 1999
· Applied Physics Letters
·
OSTI ID:20217759
Influence of dopants on defect formation in GaN
Conference
·
Mon Oct 15 00:00:00 EDT 2001
·
OSTI ID:789183