A study on high strength concrete prepared with large volumes of low calcium fly ash
This paper presents the results of a laboratory study on high strength concrete prepared with large volumes of low calcium fly ash. The parameters studied included compressive strength, heat of hydration, chloride diffusivity, degree of hydration, and pore structures of fly ash/cement concrete and corresponding pastes. The experimental results showed that concrete with a 28-day compressive strength of 80 MPA could be obtained with a water-to-binder (w/b) ratio of 0.24, with a fly ash content of 45%. Such concrete has lower heat of hydration and chloride diffusivity than the equivalent plain cement concrete or concrete prepared with lower fly ash contents. The test results showed that at lower w/b ratios, the contribution to strength by the fly ash was higher than in the mixes prepared with higher w/b ratios. The study also quantified the reaction rates of cement and fly ash in the cementitious materials. The results demonstrated the dual effects of fly ash in concrete: (1) act as a micro-aggregate and (2) being a pozzolana. It was also noted that the strength contribution of fly ash in concrete was better than in the equivalent cement/fly ash pastes suggesting the fly ash had improved the interfacial bond between the past and the aggregates in the concrete. Such an improvement was also reflected in the results of the mercury intrusion porosimetry (MIP) test.
- Research Organization:
- Hong Kong Polytechnic Univ. (CN)
- OSTI ID:
- 20075999
- Journal Information:
- Cement and Concrete Research, Vol. 30, Issue 3; Other Information: PBD: Mar 2000; ISSN 0008-8846
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of fly ash and silica fume on compression and fracture behaviors of concrete
Hydration studies of calcium sulfoaluminate cements blended with fly ash