In-situ transmission electron microscopic observation of corrosion-enhanced dislocation emission and crack initiation of stress corrosion
A constant deflection device designed for use within a transmission electron microscope (TEM) was used to study the change in dislocation configuration ahead of a crack tip during stress corrosion cracking (SCC) of brass in water, Ti-24% Al-11% Nb alloy in methanol (CH{sub 3}OH), and the initiation of SCC. In-situ tensile tests in the TEM also were carried out to assess deformation without the influence of environment. Results showed that corrosion during SCC enhanced dislocation emission, multiplication, and motion as well as produced a dislocation-free zone (DFZ). Nanocracks of SCC initiated in the DFZ or from the crack tip when the corrosion-enhanced dislocation emission and motion reached a certain condition. The action of the corrosion process prompted nanocrack propagation into a cleavage or intergranular microcrack rather than blunting into a void as seen during experiments in the TEM.
- Research Organization:
- Univ. of Science and Technology Beijing (CN)
- OSTI ID:
- 20075970
- Journal Information:
- Corrosion (Houston), Journal Name: Corrosion (Houston) Journal Issue: 5 Vol. 56; ISSN 0010-9312; ISSN CORRAK
- Country of Publication:
- United States
- Language:
- English
Similar Records
In situ observation of corrosion-enhanced dislocation emission and motion resulting in initiation of stress corrosion cracking
The in-situ TEM observation of microcrack nucleation in titanium aluminide
In-situ TEM observation of dissolution-enhanced dislocation emission, motion and the nucleation of SCC for Ti-24Al-11Nb alloy in methanol
Conference
·
Wed Dec 30 23:00:00 EST 1998
·
OSTI ID:350073
The in-situ TEM observation of microcrack nucleation in titanium aluminide
Journal Article
·
Mon Aug 01 00:00:00 EDT 1994
· Scripta Metallurgica et Materialia; (United States)
·
OSTI ID:7086773
In-situ TEM observation of dissolution-enhanced dislocation emission, motion and the nucleation of SCC for Ti-24Al-11Nb alloy in methanol
Journal Article
·
Tue Jan 14 23:00:00 EST 1997
· Scripta Materialia
·
OSTI ID:417912