Influence of pH and chloride concentration on the pitting and crevice corrosion behavior of high-alloy stainless steels
Localized corrosion resistance (pitting and crevice corrosion) of two high-alloy stainless steels (superduplex and superaustenitic) was studied in solutions with chloride concentrations of 200, 400, 600, and 6,000 ppm at pH values ranging from 2 to 6.5. Critical temperatures for pitting and crevice corrosion were calculated for these test media using electrochemical techniques (continuous current). From results obtained for cyclic polarization, the critical pitting temperature (CPT) and critical crevice temperature (CCT) of these materials in the different test media were determined. Under the tested conditions, the resistance of these materials to localized corrosion was very high. Only in test conditions of higher aggressivity (6,000 ppm CL{sup {minus}} and pH 6.5), pitting or crevice corrosion was observed. In those cases, values of pitting potential (E{sub pit}) and crevice potential (E{sub cre}) showed little tendency to decrease with an increase in CL{sup {minus}} concentration, temperature, and pH. Moreover, the CPT of these steels was determined in a ferric chloride (FeCl{sub 3}) medium, which corresponds to the standard ASTM G48 practice (Method A).
- Research Organization:
- Complutense Univ., Madrid (ES)
- OSTI ID:
- 20050522
- Journal Information:
- Corrosion (Houston), Vol. 56, Issue 4; Other Information: PBD: Apr 2000; ISSN 0010-9312
- Country of Publication:
- United States
- Language:
- English
Similar Records
Pitting and crevice corrosion of iron aluminides in a mild acid-chloride solution
Critical temperatures for crevice corrosion of high-nitrogen stainless steels