O2 structure Li{sub 2/3}[Ni{sub 1/3}Mn{sub 2/3}]O{sub 2}: A new layered cathode material for rechargeable lithium batteries. 1. Electrochemical properties
Layered Li-Mn oxide-based materials (Li{sub 2/3}[Ni{sub x}Mn{sub 1{minus}x}]O{sub 2}) with the unconventional P2 structure were prepared by ion exchanging Na for Li in the corresponding P2 structure sodium bronzes, Na{sub 2/3}(Ni{sub x}Mn{sub 1{minus}x})O{sub 2}. Powder X-ray diffraction (XRD) was used to confirm the purity and structure of the phase. The Bragg peaks from Li{sub 2/3}[Ni{sub 1/3}Mn{sub 2/3}]O{sub 2} can be indexed based on a hexagonal unit cell with dimensions a = 2.8609{angstrom} and c = 10.061{angstrom}, and the diffraction pattern can be approximately matched assuming that the atoms are in 2a and 2b positions of space group P6{sub 3}mc. However, the initial structure is more complex, because some observed diffraction peaks (i.e., 111) are forbidden in this space group. In situ XRD and electrochemical testing were used to investigate the behavior of O2-type Li{sub 2/3}[Ni{sub x}Mn{sub 1{minus}x}]O{sub 2} as a cathode for rechargeable lithium batteries. It exhibits a large reversible capacity of approximately 180 mAh/g divided into two plateaus centered near 2.8 and 3.9 V. In situ XRD proves that after an initial phase transformation, during which all forbidden diffraction peaks vanish, the extraction and insertion of lithium occurs without any first order phase transitions. The material remains layered and does not transfer to the spinel structure during cycling. It shows good capacity retention vs. cycle number at both 30 and 55 C. Differential scanning calorimetry measurements on charged electrodes show exotherms that are about one order of magnitude less intense than those from charged Li{sub x}CoO{sub 2} electrodes.
- Research Organization:
- Dalhousie Univ., Halifax, Nova Scotia (CA)
- OSTI ID:
- 20030639
- Journal Information:
- Journal of the Electrochemical Society, Vol. 147, Issue 3; Other Information: PBD: Mar 2000; ISSN 0013-4651
- Country of Publication:
- United States
- Language:
- English
Similar Records
On the P2-NaxCo1–y (Mn2/3Ni1/3)yO2 Cathode Materials for Sodium-Ion Batteries: Synthesis, Electrochemical Performance, and Redox Processes Occurring during the Electrochemical Cycling
{sup 6}Li and {sup 7}Li magic-angle spinning nuclear magnetic resonance and in situ X-ray diffraction studies of the charging and discharging of L{sub x}Mn{sub 2}O{sub 4} at 4 V