Structure and catalytic properties of VO{sub x}/MCM materials for the partial oxidation of methane to formaldehyde
Novel VO{sub x} catalysts have been developed for the partial oxidation of methane to formaldehyde by air. High surface area mesoporous siliceous MCM-41 and MCM-48 materials have been used as supports to disperse vanadium oxide to prevalent monomeric, i.e., isolated vanadium oxide species, being necessary to minimize the consecutive oxidation of the desired product to carbon oxides. On these supports, a higher concentration of isolated active sites can be obtained than on conventional silica supports. Vanadium oxide was deposited by impregnation with aqueous solutions of NH{sub 4}VO{sub 3} and VO(C{sub 2}O{sub 4}), respectively, followed by calcination of the precursor at 873 K for 16 h. The dispersity and the nature of the vanadium oxide species, i.e., their valence state, coordination, and location on and inside the pore walls, were studied by temperature-programmed reduction, potentiometric titration, solid state {sup 51}V NMR, ESR, and UV-Vis spectroscopy. FTIR spectroscopy was used to characterize the acidic properties. The catalytic properties of the catalysts were tested in a plug flow reactor. Reaction orders with respect to methane and oxygen, respectively, as well as the apparent activation energy were comparable with those reported for vanadium oxide supported on precipitated silica, pointing to similar active sites.
- Research Organization:
- Inst. fuer Angewandte Chemie Berlin-Adlershof e.V., Berlin (DE)
- OSTI ID:
- 20030521
- Journal Information:
- Journal of Catalysis, Vol. 191, Issue 2; Other Information: PBD: 25 Apr 2000; ISSN 0021-9517
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structural characteristics and reactivity properties of highly dispersed Al{sub 2}O{sub 3}/Si{sub 2} and V{sub 2}O{sub 5}/Al{sub 2}O{sub 3}/SiO{sub 2} catalysts
Synthesis, Characterization, and Catalytic Performance of Highly Dispersed Vandium Grafted SBA-15 Catalyst