Effect of plastic anisotropy on the creep strength of single crystals of a nickel-based superalloy
Journal Article
·
· Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science
The effect of plastic anisotropy, which is caused by the arrangement of slip systems, on the creep strength of notched specimens of Ni-based superalloy single crystals, is described. It was revealed that the creep strength of the notched specimens was affected by the crystallographic orientation, not only in the tensile direction, but also in the thickness direction. The creep strength was superior in the notched specimen with the [011] tensile and [01{bar 1}] plate-normal orientation, whereas the notched specimen with [011] tensile and [100] plate-normal orientation exhibited extremely poor creep strength. In the case of specimens whose tensile orientation was [011], results of the creep-rupture tests at 973 K were in agreement with the assumption of the operation of {l{underscore}brace}111{r{underscore}brace}{l{underscore}angle}112{r{underscore}angle} slip systems. The creep strength in the notched specimen with [001] tensile and [100] plate-normal orientations was superior to that in the notched specimen with [001] tensile and [011] plate-normal orientations. When the tensile orientation was [001], the results of the creep-rupture tests were in agreement with the assumption of the operation of {l{underscore}brace}111{r{underscore}brace}{l{underscore}angle}112{r{underscore}angle} slip systems during primary creep region and {l{underscore}brace}111{r{underscore}brace}{l{underscore}angle}101{r{underscore}angle} slip systems during secondary creep region.
- Research Organization:
- Tokyo Metropolitan Univ. (JP)
- OSTI ID:
- 20015619
- Journal Information:
- Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, Journal Name: Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science Journal Issue: 2 Vol. 31; ISSN 1073-5623; ISSN MMTAEB
- Country of Publication:
- United States
- Language:
- English
Similar Records
The influence of rolling practice on notch toughness and texture development in high-strength linepipe
The dislocation structure of a single-crystal {gamma} + {gamma}{prime} two-phase alloy after tensile deformation[Ni, 9.50Cr, 5.80Al, 5.36W, 5.20Co, 3.63Mo, 2.24Ti, 0.01C]
Fracture morphology of NiAl single crystals tested in tension
Journal Article
·
Tue Nov 30 23:00:00 EST 1999
· Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science
·
OSTI ID:20005973
The dislocation structure of a single-crystal {gamma} + {gamma}{prime} two-phase alloy after tensile deformation[Ni, 9.50Cr, 5.80Al, 5.36W, 5.20Co, 3.63Mo, 2.24Ti, 0.01C]
Journal Article
·
Sun Oct 31 23:00:00 EST 1999
· Materials Characterization
·
OSTI ID:20013384
Fracture morphology of NiAl single crystals tested in tension
Journal Article
·
Tue Jun 01 00:00:00 EDT 1993
· Metallurgical Transactions, A (Physical Metallurgy and Materials Science); (United States)
·
OSTI ID:6136522