Hydration and strength development of binder based on high-calcium oil shale fly ash. Part 2: Influence of curing conditions on long-term stability
The distinguishing feature of high-calcium oil shale fly ash (HCOSFA) used in experiments is the high amount of free CaO and SO{sub 3} in form of lime and anhydrite. Strength development as well as the microstructure and composition of the new formations of fly ash binder (FAB) based on HCOSFA and low-calcium coal fly ash after curing in different conditions and long-term exposure in various environments were studied. It was determined that moist air and water are the most favorable conditions for aging processes of FAB. In atmospheric air three stages in strength change of cured FAB are observed: increase of compressive strength over 1 month; sharp drop after 1 month up to the 3 to months; stabilization or slowdown of loss in strength after 3 to 6 months of exposure. The duration of the second and third stages depends on HCOSFA content and does not depend on curing conditions. One of the hydration products of FAB is ettringite. Its instability in air could be a reason for the decrease in strength of FAB and some disintegration of the hardened system. In the presence of low-calcium coal fly ash, additional amounts of stable calcium silicate hydrates are formed during FAB curing especially during steam curing. This has a positive effect on compressive strength and stability of FAB in atmospheric air.
- Research Organization:
- Ben-Gurion Univ. of the Negev, Sede-Boker (IL)
- OSTI ID:
- 20013391
- Journal Information:
- Cement and Concrete Research, Vol. 29, Issue 11; Other Information: PBD: Nov 1999; ISSN 0008-8846
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of curing conditions on the geotechnical and geochemical properties of CFBC ashes
Effects of curing temperature and NaOH addition on hydration and strength development of clinker-free CKD-fly ash binders