Migrating corrosion inhibitor blend for reinforced concrete: Part 1 -- Prevention of corrosion
The efficiency of a migrating corrosion inhibitor in preventing corrosion of mild steel was investigated in saturated calcium hydroxide (Ca[OH]{sub 2}) solutions and in mortar. The protective effect of the inhibitor against pitting corrosion caused by chloride attack and against uniform corrosion as a result of carbonation was determined. Results showed that high concentrations ({approx}10%) allowed the inhibition of pitting corrosion tritiation in solution containing 1 M/L sodium chloride (NaCl). However, inhibiting properties can be lost by evaporation of the volatile constituent of the inhibitor or by the precipitation of the nonvolatile fraction of the inhibitor in presence of calcium ions. Addition of the inhibitor blend to mortar yielded a retardation of the corrosion initiation in the case of chloride-induced corrosion, but o significant reduction in corrosion rate. No effect was found in carbonated samples, and no influence on the corrosion rate was detected. Additionally, the estimation of the extent of the retarding effect on corrosion initiation on real structures was difficult, as the inhibitor was found to evaporate from the mortar. This evaporation resulted in a loss of inhibiting properties. Hence, the long-term efficiency of the inhibitor could not be guaranteed.
- Research Organization:
- Swiss Federal Inst. of Tech., Zurich (CH)
- OSTI ID:
- 20006451
- Journal Information:
- Corrosion (Houston), Journal Name: Corrosion (Houston) Journal Issue: 12 Vol. 55; ISSN 0010-9312; ISSN CORRAK
- Country of Publication:
- United States
- Language:
- English
Similar Records
Influence of inhibitors on the corrosion cracking resistance of 65G steel wire in hydrogen sulfide solutions
PROBABILITY BASED CORROSION CONTROL FOR HIGH LEVEL WASTE TANKS: INTERIM REPORT