Influence of an aluminide coating on the TMF life of a single crystal nickel-base superalloy
Journal Article
·
· Journal of Engineering for Gas Turbines and Power
TMF tests were conducted with bare and aluminide coated single crystal nickel-based superalloy specimens. Temperature cycling was between 400 C and 1,100 C with a phase shift (135 deg) that is typical for damaged locations on turbine blades. Stress response is characterized by a constant range and the formation of a tensile mean stress as a result of relaxation in the high temperature part of the cycle which is in compression. Bare specimens showed crack initiation from typical oxide hillocks. Coated specimens showed life reduction with respect to the bare ones caused by brittle cracking of the coating in the low temperature part of the cycle. Isothermal bending tests of coated specimens confirmed the low ductility of the coating at temperatures below 600 C but quantitative correlation with the TMF test results failed.
- Research Organization:
- MTU Motoren und Turbinen Union Muenchen (DE)
- OSTI ID:
- 20006109
- Journal Information:
- Journal of Engineering for Gas Turbines and Power, Journal Name: Journal of Engineering for Gas Turbines and Power Journal Issue: 4 Vol. 121; ISSN JETPEZ; ISSN 0742-4795
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of cycle type and coating on the TMF lives of a single crystal nickel based gas turbine blade alloy
Micromechanics of failure of aluminide coated single crystal Ni superalloy under thermomechanical fatigue
Thermomechanical fatigue behavior of coated and bare nickel-based superalloy single crystals
Conference
·
Mon Dec 30 23:00:00 EST 1996
·
OSTI ID:531469
Micromechanics of failure of aluminide coated single crystal Ni superalloy under thermomechanical fatigue
Journal Article
·
Mon Sep 15 00:00:00 EDT 1997
· Scripta Materialia
·
OSTI ID:540981
Thermomechanical fatigue behavior of coated and bare nickel-based superalloy single crystals
Conference
·
Mon Dec 30 23:00:00 EST 1996
·
OSTI ID:531466