Structure and electronic states of defects in spinel of different compositions MgO{center{underscore}dot}nAl{sub 2}O{sub 3}:Me
This paper reviews the nature of defects and optical centers of magnesium aluminate spinel. The identification of absorption and luminescence bands was used to investigate the influence of UV and electron irradiation on optical center formation. Crystals examined were nominally pure MgO-nAl{sub 2}O{sub 3} crystals with compositions in the series n = 1.0, 1.5, 2.0, and 2.5. MgO{center{underscore}dot}Al{sub 2}O{sub 3} crystals doped with transition-metal ion dopants were also studied to determine the influence of impurities on the nature and concentration of lattice defects in spinel. Results strongly suggest that absorption bands at 3.78 and 4.15 eV, and luminescence bands near 5 eV, may be attributed to optical centers on antisite defects. It is also apparent that through the introduction of specific amounts of Mn and Cr ions, the concentration of optical centers (which are related to defects such as cation antisites in the spinel structure) can be considerably changed.
- Research Organization:
- Kharkov State Univ. (UA)
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 20005961
- Journal Information:
- Journal of the American Ceramic Society, Vol. 82, Issue 12; Conference: 100th Annual Meeting of the American Ceramic Society, Cincinnati, OH (US), 05/05/1998--05/06/1998; Other Information: PBD: Dec 1999; ISSN 0002-7820
- Country of Publication:
- United States
- Language:
- English
Similar Records
Cation disorder and vacancy distribution in nonstoichiometric magnesium aluminate spinel, MgO{center{underscore}dot}xAl{sub 2}O{sub 3}
Dislocations and mechanical properties of MgO-Al{sub 2}O{sub 3} spinel single crystals