Erosion-resistance of plasma sprayed coatings
Journal Article
·
· Journal of Materials Engineering and Performance
Cr{sub 3}C{sub 2}/NiCr, ZrO{sub 2}/NiCr, WTiC{sub 2}/NiCr, and X40 were plasma sprayed on the substrate 1Cr18NI9Ti in order to solve the erosion wear at high temperature encountered in the oil-refining industry. A series of properties of the coatings, including their microstructure, hardness, and erosion-behavior, have been tested. The test results show that the properties of the coatings have a significant effect on their erosion-resistant performance. Good erosion-resistant materials need to be hard and tough. Both Cr{sub 3}C{sub 2}/NiCr and X40 have good erosion resistance at elevated temperature.
- Research Organization:
- Beijing Polytechnic Univ. (CN)
- OSTI ID:
- 20005430
- Journal Information:
- Journal of Materials Engineering and Performance, Journal Name: Journal of Materials Engineering and Performance Journal Issue: 6 Vol. 8; ISSN 1059-9495; ISSN JMEPEG
- Country of Publication:
- United States
- Language:
- English
Similar Records
High-Temperature Erosive Behavior of Plasma Sprayed Cr{sub 3}C{sub 2}-NiCr/Cenosphere Coating
Abrasion and erosion wear resistance of Cr{sub 3}C{sub 2}-NiCr coatings prepared by plasma, detonation and high-velocity oxyfuel spraying
Effect of Tungsten Inert Gas Arc Remelting on Microstructure and Wear Properties of Plasma-Sprayed NiCr-Cr{sub 3}C{sub 2} Coating
Journal Article
·
Sun Apr 15 00:00:00 EDT 2018
· Journal of Materials Engineering and Performance
·
OSTI ID:22860599
Abrasion and erosion wear resistance of Cr{sub 3}C{sub 2}-NiCr coatings prepared by plasma, detonation and high-velocity oxyfuel spraying
Conference
·
Fri Dec 30 23:00:00 EST 1994
·
OSTI ID:160439
Effect of Tungsten Inert Gas Arc Remelting on Microstructure and Wear Properties of Plasma-Sprayed NiCr-Cr{sub 3}C{sub 2} Coating
Journal Article
·
Tue Oct 15 00:00:00 EDT 2019
· Journal of Materials Engineering and Performance
·
OSTI ID:22970420