High temperature deformation behavior of solid and semi-solid alloy 718
Journal Article
·
· Acta Materialia
The mechanical response of alloy 718 with various microstructures in the solid and semi-solid state has been characterized. The experimental results presented for the lower temperature solid state deformation are in good agreement with published literature values and extend the experimental range to higher temperatures and lower strain rates. When dendrites were aligned along the compression axis, the directionally solidified materials exhibited an activation energy for plastic flow consistent with the activation energy for creep and self-diffusion in nickel, even at temperatures within the mushy zone. However, samples containing non-aligned grains in the semi-solid state exhibited a greater dependence of deformation with temperature; this was associated with lubricated flow of the grains due to the intergranular liquid in the mushy zone.
- Research Organization:
- Auburn Univ., AL (US)
- OSTI ID:
- 20005417
- Journal Information:
- Acta Materialia, Journal Name: Acta Materialia Journal Issue: 18 Vol. 47; ISSN 1359-6454; ISSN ACMAFD
- Country of Publication:
- United States
- Language:
- English
Similar Records
Shear deformation behavior of Al-5% Mg in a semi-solid state
Effects of mushy zone tensile stresses on pore nucleation in superalloy 718
Modification of interdendritic convection in directional solidification by a uniform magnetic field
Journal Article
·
Thu Nov 19 23:00:00 EST 1998
· Acta Materialia
·
OSTI ID:302362
Effects of mushy zone tensile stresses on pore nucleation in superalloy 718
Book
·
Mon Dec 30 23:00:00 EST 1996
·
OSTI ID:428087
Modification of interdendritic convection in directional solidification by a uniform magnetic field
Journal Article
·
Wed Jul 01 00:00:00 EDT 1998
· Acta Materialia
·
OSTI ID:644322