In Situ Raman microscopy of chromate effects on corrosion pits in aluminum alloy
In situ, ex situ, and microscopic Raman spectroscopy were used to examine the interactions of dilute chromate solutions with actively corroding pits in aluminum alloy used for aerospace applications (AA-2024-T3). Approximately 10{sup {minus}3} M Cr(VI) in salt solution greatly reduces alloy corrosion, and soluble Cr(VI) is a major component of chromate conversion coatings (CCC). The interactions of dilute Cr(VI) with corroding alloy are likely to underlie the self-healing property of CCCs which make them so useful. Raman microscopy revealed that 10{sup {minus}3} M Cr(VI) was transported into an active pit and formed a chromate corrosion product (CCP) observable by its distinctive {approximately}850 cm{sup {minus}1} Raman band. This band was concentrated in pits and difficult to observe on the unpitted surface. Detailed spectroscopy of the CCP and several synthetic analogs revealed that the CCP is a mixed oxide of Al(III) and Cr(VI). Electrostatic bonding between the Al(OH){sub x} matrix and Cr(VI) is favored when the Al(OH){sub 3} is cationic at low pH, while covalent bonding is also possible at higher pH. The spectra of the CCP formed in AA 2024 pits implies a local pH in the region of 6 to 7. The implications of these findings to the corrosion protection mechanism of Cr(VI) on aluminum are considered.
- Research Organization:
- Ohio State Univ., Columbus, OH (US)
- OSTI ID:
- 20003942
- Journal Information:
- Journal of the Electrochemical Society, Vol. 146, Issue 11; Other Information: PBD: Nov 1999; ISSN 0013-4651
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structure and function of ferricyanide in the formation of chromate conversion coatings on aluminum aircraft alloy
Inhibition of pitting corrosion on aluminum alloy 2024-T3: Effect of soluble chromate additions vs. chromate conversion coating