Weld repair of 2-1/4Cr-1Mo service-aged header welds

Journal Article · Mon Nov 01 04:00:00 EST 1999 · Journal of Pressure Vessel Technology

DOI:https://doi.org/10.1115/1.2883713· OSTI ID:20003791

Viswanathan, R; Gandy, D; Findlan, S

The objective of this investigation was to evaluate the efficacy of different weld repair techniques as applied to service-aged 2-1/4Cr-1Mo steel weldments. A header which had been in service for 244,000 h at 1,050 F (565 C) was utilized for the study. Three girth welds were partially excavated and subjected to repairs using gas tungsten arc welding (GTAW), shielded metal arc welding (SMAW) with postweld heat treatment (PWHT), and without postweld heat treatment using a temperbead technique. Results show that all the weld repairs improved the creep rupture lives of the ex-service weldments and that remaining lives of several decades could be achieved in the repaired condition. The SMAW-temperbead repairs resulted in increase of future life, tensile strength, and impact toughness compared to the SMAW-PWHT repairs. The GTAW-PWHT repairs also produced a superior combination of mechanical properties. Remaining creep rupture lives were a function of the extrapolation procedure and specimen size. These results are described here and discussed in comparison with results previously reported for a less severely degraded condition of the steel in order to delineate the effect of prior degradation on weld repair performance.

• Research Organization: Electric Power Research Inst., Palo Alto, CA (US)
• OSTI ID: 20003791
• Journal Information: Journal of Pressure Vessel Technology, Journal Name: Journal of Pressure Vessel Technology Journal Issue: 4 Vol. 121; ISSN 0094-9930; ISSN JPVTAS
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
COMPARATIVE EVALUATIONS
GAS TUNGSTEN-ARC WELDING
HEAT TREATMENTS
MECHANICAL PROPERTIES
REPAIR
SERVICE LIFE
SHIELDED METAL-ARC WELDING
STEEL-CR2MO
WELDED JOINTS