Synthesis and cyclic oxidation behavior of a (Ni, Pt) Al coating on a desulfurized Ni-base superalloy
The influences of sulfur impurities and Pt incorporation on the scale adhesion behavior of aluminide coatings were studied and compared. Low-sulfur NiAl coatings were prepared on a desulfurized, yttrium-free, single-crystal Ni-based superalloy by a modified version of a conventional aluminizing procedure based on chemical vapor deposition. The sulfur level in the resulting NiAl coatings was measured to be less than {approximately}0.5 ppmw by glow-discharge mass spectroscopy. Platinum-modified aluminide coatings were synthesized by first electroplating a thin layer of Pt({approximately}7 {micro}m) on the superalloy, followed by the same low-sulfur aluminizing procedure. The measured sulfur content in the (Ni,Pt)Al coating was substantially higher than that of the low-sulfur NiAl coating due to contamination during the Pt electroplating process. A very adherent {alpha}-Al{sub 2}O{sub 3} scale formed on the grain surfaces of the low-sulfur NiAl coating during cyclic oxidation testing at 1,150 C, but scale spallation eventually occurred over many of the NiAl grain boundaries. In contrast, despite the higher level of sulfur in the (NI,Pt)Al coating, a very adherent scale was formed over both the coating grain surfaces and grain boundaries during thermal cycling. These results suggest that Pt additions can mitigate the detrimental influence of sulfur on scale adhesion.
- Research Organization:
- Univ. of Tennessee, Knoxville, TN (US)
- Sponsoring Organization:
- US Department of Energy
- DOE Contract Number:
- AC05-96OR22464
- OSTI ID:
- 20002012
- Journal Information:
- Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science, Journal Name: Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science Journal Issue: 10 Vol. 30; ISSN MMTAEB
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of Platinum Additions and Sulfur Impurities on the Microstructure and Scale Adhesion Behavior of Single-Phase CVD Aluminide Bond Coatings
Desulfurization of Ni-based super alloys by combined heating and glow discharge