Changes in the degree of LRO in B2-ordered intermetallic FeAl[Long Range Order]
Changes in the degree of long-range order (LRO) have been investigated in B2-ordered intermetallic Fe-44.8at%Al by electrical resistivity measurement (resistometry). Order variations were observed during isochronal annealing for different states of initial thermal treatment. A complicated behavior of resistivity changes with temperature is observed when starting with a small degree of disorder. Very slight re-ordering is found already at about 470K and is surprisingly followed by a slight disordering above 530K. Only for very long annealing times the expected ordering tendency is observed in this temperature range. Above 710K re-ordering is continued and reversible equilibrium changes of order with temperature are observed above 830K.
- Research Organization:
- Univ. of Vienna (AT)
- OSTI ID:
- 20001653
- Report Number(s):
- CONF-981104-; ISBN 1-55899-458-0; ISSN 1067-9995; TRN: IM0001%%90
- Resource Relation:
- Conference: High-Temperature Ordered Intermetallic Alloys VIII, Materials Research Society Symposium Proceedings, Boston, MA (US), 11/30/1998--12/03/1998; Other Information: PBD: 1999; Related Information: In: High-temperature ordered intermetallic alloys VIII. Materials Research Society symposium proceedings: Volume 552, by George, E.P.; Mills, M.J.; Yamaguchi, Masaharu [eds.], [600] pages.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Kinetics of defect recovery and long-range ordering in Ni{sub 3}Al + B. 1: Simultaneous recovery and ordering in cold-rolled material
Kinetics of ordering in Cu{sub 3}Au