Calorimetric studies of the energetics of order-disorder in the system Mg{sub 1{minus}x}Fe{sub x}Ca(CO{sub 3}){sub 2}
Journal Article
·
· American Mineralogist
Calorimetric studies by Chai and Navrotsky (1996) on dolomite-ankerite energetics have been extended by including two additional types of samples: a very disordered stoichiometric MgCa(CO{sub 3}){sub 2} prepared from low-temperature aqueous solution and three largely ordered natural samples of intermediate iron content. Combining these data with previous work, the authors see three distinct energetic trends. These represent samples with nearly complete order, nearly complete disorder, and intermediate order. From these trends, the enthalpy of complete disordering is estimated to be 33 {+-} 6 kJ/mol for MgCa(CO{sub 3}){sub 2} and 18 {+-} 5 kJ/mol for FeCa(CO{sub 3}){sub 2}.
- Research Organization:
- Univ. of California, Davis, CA (US)
- Sponsoring Organization:
- US Department of Energy
- OSTI ID:
- 20000953
- Journal Information:
- American Mineralogist, Journal Name: American Mineralogist Journal Issue: 10 Vol. 84; ISSN AMMIAY; ISSN 0003-004X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Calorimetric Studies of the Energetics of Order-Disorder in the System Mg(1-x)Fe(x)Ca(CO(3))(2)
Synthesis, characterization, and energetics of solid solution along the dolomite-ankerite join, and implications for the stability of ordered CaFe(CO{sub 3}){sub 2}
A combined calorimetric and computational study of the energetics of rare earth substituted UO2 systems
Journal Article
·
Tue Feb 09 23:00:00 EST 1999
· American Mineralogist
·
OSTI ID:3566
Synthesis, characterization, and energetics of solid solution along the dolomite-ankerite join, and implications for the stability of ordered CaFe(CO{sub 3}){sub 2}
Journal Article
·
Sun Sep 01 00:00:00 EDT 1996
· American Mineralogist
·
OSTI ID:543075
A combined calorimetric and computational study of the energetics of rare earth substituted UO2 systems
Journal Article
·
Mon Jul 13 00:00:00 EDT 2015
· Acta Materialia
·
OSTI ID:1370874