Solid Phase Processing of Lead-Free Brass with Carbon Additives
- Pacific Northwest National Laboratory (PNNL), Richland, WA (United States)
Currently, “lead-free” brass alloys (like C27450/C27451/C6930), used extensively in drinking water fixtures and automotive, electrical, and electronic applications contain maximum 0.25% lead to maintain mechanical performance and machinability. Adding graphite to brass as an alternative to lead, using casting, powder metallurgy, and extrusion methods, has been explored previously. However, all these methods have proven to be energy-, time-, and resource-intensive, while not enabling performance equivalent to that of C36000 brass. In this project, we developed a one-step approach using friction extrusion and ShAPE to make lead-free brass/graphite components such as wires, rods and tubes with mechanical performance equivalent to commercial lead-free brass alloys. Manufacturing temperatures were maintained ~550-730 °C with feed rates ranging between 4 – 25 mm/min. Results show larger grains at the center of the rods and wires with smaller grains developing at the edges. Graphite particles were sheared in the direction of extrusion with higher strains observed towards the edges. Hardness of the brass/graphite samples was over 25% higher than that of the corresponding brass-only samples (rods and wires), also friction extruded. Our results show that the sub-micron graphite plays an important role in limiting process temperature and restraining grain growth during friction extrusion, thus reducing grain size in composites.
- Research Organization:
- Pacific Northwest National Laboratory (PNNL), Richland, WA (United States)
- Sponsoring Organization:
- USDOE Laboratory Directed Research and Development (LDRD) Program
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1983976
- Report Number(s):
- PNNL--33415
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructural Evolution and Mechanical Behavior of Lead-Free Silicon Brass Manufactured by Low-Pressure Die Casting
Material flow behavior and microstructural refinement of AA6061 alloy during friction extrusion
Eliminating Yield Anisotropy and Enhancing Ductility in Mg Alloys by Shear Assisted Processing and Extrusion
Journal Article
·
Mon Oct 15 00:00:00 EDT 2018
· Journal of Materials Engineering and Performance
·
OSTI ID:22863258
Material flow behavior and microstructural refinement of AA6061 alloy during friction extrusion
Journal Article
·
Sun Aug 20 20:00:00 EDT 2023
· Materials Characterization
·
OSTI ID:2377266
Eliminating Yield Anisotropy and Enhancing Ductility in Mg Alloys by Shear Assisted Processing and Extrusion
Conference
·
Sun Feb 28 23:00:00 EST 2021
·
OSTI ID:1808506