Formation and Consolidation of UN Nanostructures in U-Mo Fuel via Mechanical Alloying and Spark Plasma Sintering
- Idaho National Laboratory
Uranium-molybdenum (U-Mo) alloys show promise as a nuclear fuel system due to their high thermal conductivity and high fuel loading capability. However, U-Mo systems suffer from irradiation induced swelling ultimately affecting the cladding via mechanical and chemical interaction. To address these shortcomings, this thesis investigated the formation of uranium mononitride (UN) nanoparticles within a U-10Mo matrix. To promote the formation of UN, U-10Mo powders were mechanically alloyed under a high purity nitrogen cover gas (99.9995%) atmosphere. Variations were made in stainless steel milling media size, duration of milling, and number of times the milling jar was re-aerated with nitrogen gas. UN nanoparticulates were successfully formed within the U-Mo matrix and was characterized utilizing light element analysis, X-ray diffractometry, scanning and transmission-electron microscopy, electron energy loss spectroscopy, and atom probe tomography. Presence of the UN nanoparticles was found as early as 1-hour into the mechanical alloying process, and significant iron contamination found after 10-hours of milling. The U-Mo/UN powders were compacted using spark plasma sintering techniques in order to stabilize the nanostructure. U-Mo/UN compacts containing small amounts of neodymium and helium were analyzed to observe the defect migration tendencies of fission products within the fuel.
- Research Organization:
- Idaho National Lab. (INL), Idaho Falls, ID (United States)
- Sponsoring Organization:
- USDOE Office of Nuclear Energy (NE)
- DOE Contract Number:
- DE-AC07-05ID14517
- OSTI ID:
- 1983625
- Report Number(s):
- INL/RPT-23-72383-Rev000
- Country of Publication:
- United States
- Language:
- English
Similar Records
Uranium nitride (UN) pellets with controllable microstructure and phase – fabrication by spark plasma sintering and their thermal-mechanical and oxidation properties
Design and fabrication of high density uranium dispersion fuels.