Comparing Neutron and Ion Irradiation by Atom Probe Tomography and In-situ Electron Microscopy [Slides]
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
Stainless steel TPBAR components undergo neutron radiation-induced segregation and dislocation loop formation. Comparison experiments with ion beams accelerate the damage, and visualize the damage process with in-situ microscopy. In-situ Au irradiation causes defect formation, but no elemental segregation.
- Research Organization:
- Sandia National Laboratories (SNL-NM), Albuquerque, NM (United States)
- Sponsoring Organization:
- USDOE National Nuclear Security Administration (NNSA)
- DOE Contract Number:
- NA0003525
- OSTI ID:
- 1888138
- Report Number(s):
- SAND2021-11606C; 699487
- Country of Publication:
- United States
- Language:
- English
Similar Records
In situ transmission electron microscopy with dual ion beam irradiation and implantation
In-situ and ex-situ characterization of ion-irradiated AM materials
In Situ TEM Multi-Beam Ion Irradiation as a Technique for Elucidating Synergistic Radiation Effects
Journal Article
·
Wed Jan 13 19:00:00 EST 2021
· Materials Characterization
·
OSTI ID:1780693
In-situ and ex-situ characterization of ion-irradiated AM materials
Technical Report
·
Sat Jul 01 00:00:00 EDT 2023
·
OSTI ID:1992453
In Situ TEM Multi-Beam Ion Irradiation as a Technique for Elucidating Synergistic Radiation Effects
Journal Article
·
Fri Sep 29 00:00:00 EDT 2017
· Materials
·
OSTI ID:1422341