Elevated temperature creep properties of NiAl cryomilled with and without Y2O3
The creep properties of lots of NiAl cryomilled with and without Y2O3 have been determined in compression and tension. Although identical cryomilling procedures were used, differences in composition were found between the lot ground with 0.5 vol% yttria and the lot ground without Y2O3. Compression testing between 1000 and 1300 K yielded similar creep strengths for both materials, while tensile creep rupture testing indicated that the yttria-containing alloy was slightly stronger than the Y2O3-free version. Both compression and tensile testing showed two deformation regimes; whereas the stress state did not affect the high stress exponent (n approximately equals 10) mechanism, the low stress exponent regime n was approximately 6 in tension and approximately 2 in compression. The strengths in tension were somewhat less than those measured in compression, but the estimated activation energies (Q) of approximately 600 kJ/mol for tensile testing were closer to the previously measured values (approximately 700 kJ/mol) for NiAl-AlN and very different from the Q`s of 400 and 200 kJ/mol for compression tests in the high and low stress exponent regimes, respectively. A Larson-Miller comparison indicated that cryomilling can produce an alloy with long-term, high-temperature strength at least equal to conventional superalloys.
- Research Organization:
- National Aeronautics and Space Administration, Cleveland, OH (United States). Lewis Research Center
- OSTI ID:
- 188478
- Report Number(s):
- N--96-17171; NASA-TM--111192; NAS--1.15:111192; NIPS--96-07165
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructure and strengthening of creep-tested cryomilled NiAl-AlN
NiAl-base composite containing high volume fraction of AlN particulate for advanced engines