Effect of zinc additions on oxide rupture strain and repassivation kinetics of iron-based alloys in 288 C water
- General Electric Corporate Research and Development Center, Schenectady, NY (United States)
The effect of Zn water chemistry additions on the mechanism of intergranular stress corrosion cracking (IGSCC) of Fe-based alloys in water at 288 C was evaluated in terms of the slip-dissolution model. In this model, an increase in the oxide film rupture strain or surface film repassivation kinetics improved resistance to IGSCC. The oxide rupture strain of type 304L (UNS S30403) stainless steel (SS) increased up to a factor of two in deaerated and 200 ppb oxygenated, high-purity water (< 0.08 {micro}S/cm outlet) after exposure to Zn concentrations up to 60 ppb for 30 h to 170 h and at 20 ppb Zn for > 300 h of exposure. Repassivation kinetics experiments showed Zn additions of {approximately} 100 ppb increased the repassivation rate of an Fe-12% Cr alloys up to a factor of two in various deaerated water environments at 288 C. Life prediction modeling revealed that the combination of a more ductile oxide film and faster repassivation kinetics resulted in a reduction in the overall crack growth rate (CGR) by at least a factor of four. This factor of improvement was consistent with data from compact tension experiments in similar environments where CGR decreased as the Zn addition increased, with a greater decrease in CGR realized at lower pre-Zn CGR.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 187039
- Journal Information:
- Corrosion, Journal Name: Corrosion Journal Issue: 1 Vol. 52; ISSN 0010-9312; ISSN CORRAK
- Country of Publication:
- United States
- Language:
- English
Similar Records
Repassivation and crack propagation of alloy 600 in 288 C water
Repassivation and crack propagation of alloy 600 in 288 C water