Structure and magnetic properties of Sm{sub 3}(Fe{sub 0.85}Cr{sub 0.15}){sub 29}N{sub y} alloys
Journal Article
·
· IEEE Transactions on Magnetics
- Minebea Co., Ltd., Iwata, Shizuoka (Japan). Research and Development Center
The structure and magnetic properties of Sm{sub 3}(Fe{sub 0.85}Cr{sub 0.15}){sub 29}N{sub y} alloy were investigated. It was found that the alloy had the R{sub 3}(Fe,M){sub 29}-type structure and absorbed 4--5 wt.% of nitrogen which exceeds 4 nitrogen atoms per unit formula. The coercivity of the powder was greatly influenced by the nitrogen content and annealing. The Sm{sub 3}(Fe{sub 0.85}Cr{sub 0.15}){sub 29}N{sub y} alloy powder with 4.1 wt.% of nitrogen showed a high coercivity of 552 kA/m without fine grinding.
- OSTI ID:
- 186950
- Report Number(s):
- CONF-950404-; ISSN 0018-9464; TRN: IM9609%%223
- Journal Information:
- IEEE Transactions on Magnetics, Vol. 31, Issue 6Pt2; Conference: Conference on magnetism and magnetic materials, San Antonio, TX (United States), 18-21 Apr 1995; Other Information: PBD: Nov 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Structure and magnetic properties of Sm{sub 2}(Fe,Mn){sub 17}N{sub x} coarse powders with high coercivity
Plasma carbonitriding reaction characteristics of Sm{sub 2}Fe{sub 17}
Dependence of the magnetic properties of Zn bonded Sm{sub 2}Fe{sub 17}N{sub x} magnets on the particle size distribution
Journal Article
·
Tue Apr 01 00:00:00 EST 1997
· Journal of Applied Physics
·
OSTI ID:186950
+1 more
Plasma carbonitriding reaction characteristics of Sm{sub 2}Fe{sub 17}
Journal Article
·
Tue Nov 01 00:00:00 EST 1994
· Chemistry of Materials
·
OSTI ID:186950
Dependence of the magnetic properties of Zn bonded Sm{sub 2}Fe{sub 17}N{sub x} magnets on the particle size distribution
Journal Article
·
Tue Mar 01 00:00:00 EST 1994
· IEEE Transactions on Magnetics
·
OSTI ID:186950
+1 more