Effect of Stress on Irradiation Responses of Highly Oriented Pyrolytic Graphite
The effect of stress on irradiation responses of highly oriented pyrolytic graphite (HOPG) was studied by combing molecular dynamics (MD) simulation, proton irradiation, and Raman characterization. MD simulations of carbon knock-on at energies < 60 eV were used to obtain average threshold displacement energies ($$\overline{E}$$d) as a function of strain ranging from 0 to 10%. Simulations at a higher irradiation energy of 2–5 keV were used to study the effect of strain on damage cascade evolution. With increasing tensile strain,$$\overline{E}$$d was reduced from 35 eV at 0% strain to 31 eV at 10% strain. The strain-reduced $$\overline{E}$$d led to a higher damage peak and more surviving defects (up to 1 ps). Furthermore, high strains induced local cleavage around the cavities, as one additional mechanism of damage enhancement. Experimentally, HOPG film was folded, and the folded region with the maximum tensile stress was irradiated by a 2 MeV proton beam. Raman characterization showed significantly enhanced D to G modes in comparison to the stress-free irradiation. Based on the strain dependence of $$\overline{E}$$d and the Kinchin–Pease model, a formula for displacement estimation under different tensile strains is proposed. The stress effects need to be considered in graphite applications in a reactor’s harsh environment where both neutron damage and stress are present.
- Research Organization:
- Texas A & M Univ., College Station, TX (United States). Texas A & M Engineering Experiment Station
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- Grant/Contract Number:
- SC0006725
- OSTI ID:
- 1867075
- Alternate ID(s):
- OSTI ID: 1904508
- Journal Information:
- Materials, Journal Name: Materials Vol. 15 Journal Issue: 10; ISSN 1996-1944
- Publisher:
- MDPI AGCopyright Statement
- Country of Publication:
- Switzerland
- Language:
- English
Similar Records
Low-energy D{sup +} and H{sup +} ion irradiation effects on highly oriented pyrolytic graphite
Defect Production, Multiple Ion-Solid Interactions and Amorphization in SiC