Progress Report on Graphite-Salt Interaction Studies (FY21)
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
This report summarizes the activities performed in FY21 to investigate the interactions between nuclear graphite and molten salts, such as FLiNaK. First, building on last year’s achievements, the team improved the procedure for measurements on pressurized salt intrusion in nuclear graphite and performed new experiments at variable pressures with specimens of different sizes and shapes. Additionally, the team actively provided suggestions and comments for ASTM D8091, Standard Guide for Impregnation of Graphite with Molten Salts, which came up for periodic revision in 2021. Second, the team expanded its capabilities to further characterize salt-impregnated graphite by procuring and installing a laser-induced breakdown spectroscopy (LIBS) instrument capable of producing a 3D chemical composition of a surface and subsurface region of specimens. A methodology for accurately analyzing information was developed, and a manuscript was submitted for publication. The LIBS instrument sample cell is sealed in controlled inert atmosphere, which is an advantage for using humidity-sensitive samples and Be-contaminated samples. This aligns with the team’s effort to expand the capabilities of handling FLiBe and Becontaining materials in two newly installed glovebox units. Third, the team performed preliminary tribology tests for pebble graphite wear in contact with stainless steel in dry state and in molten salt at high temperature. These tests are needed to establish the baseline for the wear of pebble graphite by friction against metallic walls. The friction and wear of pebbles in the fluoride salt-cooled hightemperature reactor are expected to generate dust, which is a concern for other components’ properties and safe reactor operation.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-00OR22725
- OSTI ID:
- 1828250
- Report Number(s):
- ORNL/TM-2021/2247
- Country of Publication:
- United States
- Language:
- English
Similar Records
Report on Initial Tribological Studies of Graphite in Dry Argon and Molten Salt Environment
Friction and wear of nuclear graphite exposed to molten FLiNaK salt environment
Examining Graphite Degradation in Molten Salt Environments: A Chemical, Physical, and Material Analysis
Technical Report
·
Sun Dec 31 23:00:00 EST 2023
·
OSTI ID:2283836
Friction and wear of nuclear graphite exposed to molten FLiNaK salt environment
Technical Report
·
Mon Jun 30 20:00:00 EDT 2025
·
OSTI ID:3002306
Examining Graphite Degradation in Molten Salt Environments: A Chemical, Physical, and Material Analysis
Technical Report
·
Sat Aug 17 00:00:00 EDT 2024
·
OSTI ID:2474875