Quantitative characterization of the fracture surface of Si single crystals by confocal microscopy
- Univ. of Illinois, Urbana, IL (United States)
Experiments are conducted to study the dislocation nucleation conditions at the crack tip in {l_brace}110{r_brace}<110> oriented Si single crystals. Specimens with surface cracks are first statically loaded at elevated temperatures for a prolonged period of time to initiate and move dislocations away from the crack tip, then cooled down to room temperature and loaded to fracture to measure the fracture toughness. Fractographic analysis of the fracture surfaces is performed. Distinct wavy patterns on the fracture surface at the initial cleavage crack front are observed, which is attributed to the existence of local mixed mode 1/mode 3 stresses resulting from the inhomogeneous dislocation activity. Confocal microscopy is employed to quantify the fracture surface roughness. The results show that the increase of fracture toughness is directly associated with the increased area of the rough surface, which is characterized by the roughness number or the fractal dimension increment. The results also demonstrate that dislocation nucleation can occur only at discrete sites. The spacing between these dislocation nucleation sources is of the order of 1 {micro}m. A simple model is developed for the relationship between the fracture toughness and the surface roughness parameters, which is in good agreement with the experimental results.
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- FG02-91ER45439
- OSTI ID:
- 177973
- Journal Information:
- Journal of the American Ceramic Society, Journal Name: Journal of the American Ceramic Society Journal Issue: 12 Vol. 78; ISSN 0002-7820; ISSN JACTAW
- Country of Publication:
- United States
- Language:
- English
Similar Records
Investigations of loaded crack tips in NiAl by atomic force microscopy
Slip systems and dislocation emission from crack tips in single crystal TiC at low temperatures