Si-based materials for lithium-ion batteries VI. 15% surface-modified Si/C-graphite/carbon black/lithiated polyacrylic acid electrode
X-ray photoelectron spectroscopy was used to analyze a 15%Si/C-graphite/carbon black/lithiated polyacrylic acid electrode fabricated at the Cell Analysis, Modeling, and Prototyping Facility (CAMP), Argonne National Laboratory. The spectra were obtained using incident monochromatic Al Kα radiation at 1486.6 eV (0.83 401 nm). An initial survey spectrum together with O 1s, C 1s, and Si 2p are presented. A final survey spectrum was collected to ascertain the amount of beam-induced damage, which appears to be minimal. The spectra indicate the principal core level photoelectron and Auger electron signals with only minor nitrogen and lithium signals and show the expected silicon-carbon species related to the surface modification process in addition to oxidized carbon and silicon due to atmospheric exposure as well contributions related to the binder material.
- Research Organization:
- Argonne National Laboratory (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE), Transportation Office. Vehicle Technologies Office; USDOE
- Grant/Contract Number:
- AC02-06CH11357
- OSTI ID:
- 1774526
- Alternate ID(s):
- OSTI ID: 1618783
- Journal Information:
- Surface Science Spectra, Vol. 27, Issue 1; ISSN 1055-5269
- Publisher:
- American Vacuum Society - AIPCopyright Statement
- Country of Publication:
- United States
- Language:
- English
Similar Records
Si-based materials for lithium-ion batteries VII. 70% surface-modified Si/C-carbon black/lithiated polyacrylic acid electrode
Si-based materials for lithium-ion batteries VIII. 90% surface-modified Si/C-lithiated polyacrylic acid electrode