Si-based materials for lithium-ion batteries IX: 70% surface-modified Si/C/polyethylene glycol-carbon black/lithiated polyacrylic acid electrode
- Univ. of Illinois at Urbana-Champaign, IL (United States)
- Argonne National Lab. (ANL), Argonne, IL (United States)
X-ray photoelectron spectroscopy was used to analyze a 70% Si/C-carbon black/polyethylene glycol/lithiated polyacrylic acid electrode fabricated at the Cell Analysis, Modeling, and Prototyping Facility (CAMP), Argonne National Laboratory. The spectra were obtained using incident monochromatic Al Kα radiation at 1486.6 eV (0.834 01 nm). An initial survey spectrum together with O 1s, C 1s, and Si 2p are presented. A final survey scan was collected to ascertain the amount of beam-induced damage, which appears to be minimal. Finally, the spectra indicate the principal core level photoelectron and Auger electron signals with only minor copper and lithium signals and show the expected silicon-carbon species related to the surface modification process in addition to oxidized carbon and silicon due to atmospheric exposure as well as contributions related to the binder material.
- Research Organization:
- Argonne National Laboratory (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE), Transportation Office. Vehicle Technologies Office; USDOE
- Grant/Contract Number:
- AC02-06CH11357
- OSTI ID:
- 1774522
- Alternate ID(s):
- OSTI ID: 1618790
- Journal Information:
- Surface Science Spectra, Vol. 27, Issue 1; ISSN 1055-5269
- Publisher:
- American Vacuum Society - AIPCopyright Statement
- Country of Publication:
- United States
- Language:
- English
Similar Records
Si-based materials for lithium-ion batteries VIII. 90% surface-modified Si/C-lithiated polyacrylic acid electrode
Si-based materials for lithium-ion batteries X: 70% surface-modified Si/C/polyvinylidine difluoride-carbon black/lithiated polyacrylic acid electrode