Fracture resistance measurement of advanced ceramics at elevated-temperatures using Chevron-notched specimens and other novel techniques
- Univ. of Washington, Seattle, WA (United States)
The quasi-static fracture behavior of advanced ceramics was assessed in the temperature range of 20{degrees} to 1400{degrees}C. Chevron-notched, three-point flexure specimens and a laser-based CMOD measurement systems were used in testing. Types of materials characterized included monolithic ceramics (SiC, Si{sub 3}N{sub 4}, MgAl{sub 2}O{sub 4}), self-reinforced monoliths (acicular-grained Si{sub 3}N{sub 4}, acicular grained mullite), and ceramic matrix composites (SiC whisker/Al{sub 2}O{sub 3} matrix, TiB{sub 2} particulate/SiC matrix, SiC fibre/CVI SiC matrix, Al{sub 2}O{sub 3} fibre/CVI SiC matrix). Fracture resistance behaviour of the materials was quantified as three distinct regimes of the fracture histories. At crack initiation, the apparent fracture toughness was evaluated as the critical stress intensity factor, K{sub IC}. During stable crack propagation, the crack growth resistance was characterized by the instantaneous strain energy release rate, G{sub R} using a compliance method assuming linear-elastic unloading to calculate the effective crack lengths. At final fracture, the complete fracture process was quantified using the work-of-fracture, WOF, which can be equated to the fracture surface energy for linearelastic materials. Results indicate that the chevron-notched, three-point flexure specimen facilitates the study of fracture behavior in a wide range of brittle and quasi-brittle materials at elevated temperatures. The unique features of the chevron geometry, which are automatic, in-situ crack initiation and inherent stable crack growth, are crucial to the successful evaluation of the fracture tests.
- OSTI ID:
- 175211
- Report Number(s):
- CONF-950686-; TRN: 95:006111-0132
- Resource Relation:
- Conference: Joint applied mechanics and materials summer meeting, Los Angeles, CA (United States), 28-30 Jun 1995; Other Information: PBD: 1995; Related Information: Is Part Of AMD - MD `95: Summer conference; PB: 520 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Elevated-temperature fracture resistances (K sub IC , R-curves,. gamma. sub. omega. OF ) of monolithic and composite ceramics using chevron-notched, bend tests
Fracture Toughness of Advanced Structural Ceramics: Applying ASTM C1421