Stability of zirconium hydride
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
This reports complete Milestone M2.2.1 Stability of zirconium hydride: Experimental investigation of the hydrogen concentration of encapsulated zirconium hydride before and after joining. In this milestone, we first report the successful fabrication of crack-free bulk zirconium hydride by using the ORNL static hydriding system. The fabricated hydride was characterized by using X-ray diffraction (XRD) and X-ray computed tomography (XCT). XRD results showed that the δ-phase zirconium hydride, α-zirconium, and ε-phase hydride were present. XCT confirmed the absence of the internal cracking. The hydrogen concentration was determined by the weight change before and after hydrogen loading, given the fact that the oxide phase was not found during XRD analysis. Two metallic cladding materials, i.e., molybdenum and FeCrAl, were selected to encapsulate the fabricated zirconium hydride pellets. Demonstration capsules were designed and machined. Mo crucible was successfully sealed by using a combination of electron beam welding and gas tungsten arc welding. Due to the undesired neutronics property of Mo, further investigation of this cladding material was not pursued. Electron beam welding and laser beam welding were employed to seal the FeCrAl capsules. XRD were performed on the zirconium hydride before and after the sealing. The results showed that the welding process has negligible impact on the hydrogen content in the FeCrAl-canned zirconium hydride. The presented work fulfilled the proposed work under this milestone and paves a pathway to fabricate single-phase zirconium hydride and to develop robust cladding materials to can bulk zirconium hydride.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Advanced Research Projects Agency - Energy (ARPA-E)
- DOE Contract Number:
- AC05-00OR22725
- OSTI ID:
- 1651341
- Report Number(s):
- ORNL/SPR-2020/1485
- Country of Publication:
- United States
- Language:
- English
Similar Records
Produce ZrH Moderator Material
Downselection of Cladding Materials for Zirconium Hydride Moderator
Technology Enabling Zero-EPZ Micro Modular Reactors: Fabrication of Zirconium Hydride with Controlled Hydrogen Loading
Technical Report
·
Thu Mar 11 23:00:00 EST 2021
·
OSTI ID:1805015
Downselection of Cladding Materials for Zirconium Hydride Moderator
Technical Report
·
Thu Mar 11 23:00:00 EST 2021
·
OSTI ID:1886517
Technology Enabling Zero-EPZ Micro Modular Reactors: Fabrication of Zirconium Hydride with Controlled Hydrogen Loading
Technical Report
·
Sat Sep 12 00:00:00 EDT 2020
·
OSTI ID:1879976