Comparison of selective oxidation in Ni-based alloys exposed to PWR primary water and Rhines Pack environments
Conference
·
OSTI ID:1605406
- BATTELLE (PACIFIC NW LAB)
A mechanistic understanding of corrosion and oxidation processes is crucial to ensure long-term resistance to stress corrosion cracking of Ni-based structural alloys in PWR primary and secondary systems. Aqueous corrosion of complex Ni-based alloys under PWR water conditions as well as gaseous oxidation of low-solute Ni binary alloys at high temperatures (>800 °C) have been studied extensively. However, a significant knowledge gap exists between response of Ni-based alloys in aqueous and gaseous environmental conditions. Selective oxidation at different temperatures was investigated in a series of gaseous Rhines Pack experiments for a high-purity Ni-5Cr binary alloy and a commercial Ni-18Cr-9Fe Alloy 600. Focused ion beam milling enabled the extraction of site-specific specimens containing high-energy grain boundaries. Analytical transmission electron microscopy was employed to analyze the microstructure and chemical composition of the resulting localized oxidation. The oxidation mechanism in the gaseous Rhines Pack atmosphere at 420 °C included the formation of a protective Cr-oxide cap above grain boundaries in all cases. At higher temperatures (600 and 800 °C), penetrative intergranular and transgranular internal oxidation was observed. Direct comparisons are made to corrosion response for these same materials in simulated PWR primary water at 320-360 °C. These results reveal a temperature dependence for gaseous oxidation and indicate mechanistic differences between aqueous and gaseous degradation in Ni-Cr alloys. These results imply that selective intergranular corrosion in PWR water is governed by processes beyond mere oxidation. Consideration of complex corrosion/dissolution processes at surfaces and in open cracks is essential for the better understanding of stress corrosion cracking mechanisms in PWR primary water.
- Research Organization:
- Pacific Northwest National Laboratory (PNNL), Richland, WA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1605406
- Report Number(s):
- PNNL-SA-146936
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of Applied Stress on the Selective Oxidation of Alloy 600 Exposed to PWR Primary Water and Rhines Pack Environments
(The role of grain boundary chemistry and structure in the environmentally-assisted intergranular cracking of nickel-base alloys)
Examinations of Oxidation and Sulfidation of Grain Boundaries in Alloy 600 Exposed to Simulated Pressurized Water Reactor Primary Water
Conference
·
Wed Sep 28 00:00:00 EDT 2022
·
OSTI ID:1894579
(The role of grain boundary chemistry and structure in the environmentally-assisted intergranular cracking of nickel-base alloys)
Technical Report
·
Sun Dec 31 23:00:00 EST 1989
·
OSTI ID:6452413
Examinations of Oxidation and Sulfidation of Grain Boundaries in Alloy 600 Exposed to Simulated Pressurized Water Reactor Primary Water
Journal Article
·
Wed Apr 17 00:00:00 EDT 2013
· Microscopy and Microanalysis
·
OSTI ID:1083397