Atomic-Scale Structure and Stress Release Mechanism in Core–Shell Nanoparticles
- Department of Chemical and Biological Engineering, University of Colorado at Boulder, Boulder, Colorado 80309, United States
- Department of Physics &, Astronomy and California NanoSystems Institute, University of California, Los Angeles, California 90095, United States
According to the article, core–shell nanoparticles find applications in catalysts, sensors, and theranostics. The full internal 3D atomic structure, however, cannot be resolved by current imaging and diffraction techniques. We analyzed the atomic positions and stress-release mechanism in a cubic Au–Pd core–shell nanoparticle in approximately 1000 times higher resolution than current experimental techniques using large-scale molecular dynamics simulation to overcome these limitations. The core–shell nanocube of 73 nm size was modeled similarly to solution synthesis by random epitaxial deposition of a 4 nm thick shell of Pd atoms onto a Au core of 65 nm side length using reliable interatomic potentials. The internal structure reveals specific deformations and stress relaxation mechanisms that are caused by the +4.8% lattice mismatch of gold relative to palladium and differential confinement of extended particle facets, edges, and corners by one, two, or three Au–Pd interfaces, respectively. The three-dimensional lattice strain causes long-range, arc-like bending of atomic rows along the faces and edges of the particle, especially near the Au–Pd interface, a bulging deformation of the Pd shell, and stacking faults in the Pd shell at the corners of the particle. The strain pattern and mechanism of stress release were further characterized by profiles of the atomic layer spacing in the principal crystallographic directions. Accordingly, strain in the Pd shell is several times larger in the extended facets than near the edges and corners of the nanoparticle, which likely affects adsorption, optical, and electrochemical properties. The findings are consistent with available experimental data, including 3D reconstructions of the same cubic nanoparticle by coherent diffractive imaging (CDI) and may be verified by more powerful experimental techniques in the future. The stress release mechanisms are representative for cubic core–shell nanoparticles with fcc structure and can be explored for different shapes by the same methods.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). Oak Ridge Leadership Computing Facility (OLCF); Argonne National Lab. (ANL), Argonne, IL (United States); UT-Battelle LLC/ORNL, Oak Ridge, TN (United States); Univ. of California, Los Angeles, CA (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- DOE Contract Number:
- AC02-06CH11357; AC05-00OR22725; SC0010378
- OSTI ID:
- 1565750
- Journal Information:
- ACS Nano, Vol. 12, Issue 12; ISSN 1936-0851
- Publisher:
- American Chemical Society (ACS)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Direct Observation of Early Stages of Growth of Multilayered DNA-Templated Au-Pd-Au Core-Shell Nanoparticles in Liquid Phase
Surface-structure sensitivity of CeO2 nanocrystals in photocatalysis and enhancing the reactivity with nanogold