Glass-bonded iodosodalite waste form for immobilization of 129I
- Washington State University
- BATTELLE (PACIFIC NW LAB)
- The University of Sheffield
Immobilization of radioiodine (e.g., 129I, 131I) is an important need for current and future nuclear fuel cycles. For the current work, iodosodalite [Na8(AlSiO4)6I2] was synthesized hydrothermally from metakaolin, NaI, and NaOH. Following hydrothermal treatment, dried unwashed powders were used to make glass-bonded iodosodalite waste forms by heating pressed pellets at 650, 750, or 850 °C with two different types of sodium borosilicate glass binders, i.e., NBS-4 and SA-800. These heat-treated specimens were characterized with X-ray diffraction, Fourier-transform infrared spectroscopy, scanning electron microscopy, energy dispersive spectroscopy, thermal analysis, porosity and density measurements, neutron activation analysis, and inductively-coupled plasma mass spectrometry. The pellets mixed with 10 mass% of NBS-4 or SA-800 and heat-treated at 750 °C contained relatively high percentage iodine retention (~44-47 % of the maximum iodine loading) with relatively low porosities, while other pellets with higher percentages iodine retention either contained higher porosity or were not completely sintered. ASTM C1308 chemical durability tests of monolithic specimens showed a large initial release of Na, Al, Si, and I on the first day, possibly from water-soluble salt crystals or non-durable amorphous phases. Release rates of Na and Si were higher than for Al and I, probably due to a poorly durable Na-Si-O phase from the glass bonding matrix. The cumulative normalized release of iodine was 12.5 g m-2 for the first 10 1-d exchanges, suggestive of coherent dissolution. The average release rate from 10-24 days during the 7-d exchange intervals was 0.2336 g m-2 d-1.
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1557598
- Report Number(s):
- PNNL-SA-130829
- Journal Information:
- Journal of Nuclear Materials, Vol. 504
- Country of Publication:
- United States
- Language:
- English
Similar Records
Iodosodalite Waste Forms from Low-Temperature Aqueous Process
Iodosodalite synthesis with hot isostatic pressing of precursors produced from aqueous and hydrothermal processes