Interface Reactions Responsible for Run-out in Active Brazing: Part 2

Journal Article · Mon Oct 01 00:00:00 EDT 2018 · Welding Journal

OSTI ID:1529300

Vianco, Paul T. ^[1]; Walker, Charles A. ^[1]; De Smet, Dennis J. ^[1]; Kilgo, Alice C. ^[1]; McKenzie, Bonnie M. ^[1]; Grant, Richard L. ^[1]

---

1. Sandia National Laboratories (SNL-NM), Albuquerque, NM (United States)

This Part 2 study examined the microstructural characteristics of braze joints made between two KOVar^TM base materials using the filler metals, Ag-xAl, having x = 0, 2, 5, and 10 wt.% Al additions. Brazing processes had temperatures of 965°C (1769°F) and 995°C and brazing times of 5 and 20 min. All brazing was performed under high vacuum.

• Research Organization: Sandia National Laboratories (SNL-NM), Albuquerque, NM (United States)
• Sponsoring Organization: USDOE National Nuclear Security Administration (NNSA), Office of Defense Nuclear Security (NA-70)
• Grant/Contract Number: AC04-94AL85000
• OSTI ID: 1529300
• Report Number(s): SAND--2018-11317J; 669524
• Journal Information: Welding Journal, Journal Name: Welding Journal Vol. 2018; ISSN 0043-2296
• Publisher: American Welding Society
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE