Chemical Etch Effects on Laser-Induced Surface Damage Growth in Fused Silica
We investigated chemical etching as a possible means to mitigate the growth of UV laser-induced surface damage on fused silica. The intent of this work is to examine the growth behavior of existing damage sites that have been processed to remove the UV absorbing, thermo-chemically modified material within the affected area. The study involved chemical etching of laser-induced surface damage sites on fused silica substrates, characterizing the etched sites using scanning electron microscopy (SEM) and laser fluorescence, and testing the growth behavior of the etched sites upon illumination with multiple pulses of 351nm laser light. The results show that damage sites that have been etched to depths greater than about 9 {micro}m have about a 40% chance for zero growth with 1000 shots at fluences of 6.8-9.4 J/cm{sup 2}. For the etched sites that grow, the growth rates are consistent with those for non-etched sites. There is a weak dependence of the total fluorescence emission with the etch depth of a site, but the total fluorescence intensity from an etched site is not well correlated with the propensity of the site to grow. Deep wet etching shows some promise for mitigating damage growth in fused silica, but fluorescence does not seem to be a good indicator of successful mitigation.
- Research Organization:
- Lawrence Livermore National Laboratory (LLNL), Livermore, CA
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 15013141
- Report Number(s):
- UCRL-JC-139666
- Country of Publication:
- United States
- Language:
- English
Similar Records
Methods for Mitigating Growth of Laser-Initiated Surface Damage on Fused Silcia Optics at 351nm
Effects of wet etch processing on laser-induced damage of fused silica surfaces
Downstream Intensification Effects Associated with CO2 Laser Mitigation of Fused Silica
Conference
·
Tue Dec 11 23:00:00 EST 2001
·
OSTI ID:15002010
Effects of wet etch processing on laser-induced damage of fused silica surfaces
Conference
·
Mon Dec 21 23:00:00 EST 1998
·
OSTI ID:8359
Downstream Intensification Effects Associated with CO2 Laser Mitigation of Fused Silica
Conference
·
Mon Oct 29 00:00:00 EDT 2007
·
OSTI ID:923089