XPS Studies of Yb14MnSb11 and Yb14ZnSb11
Measurements of core and valence electronic states of single crystals of the rare earth transition metal Zintl phases Yb{sub 14}MnSb{sub 11} and Yb{sub 14}ZnSb{sub 11} were performed using the X-ray photoelectron spectroscopy station of Beamline 7 at the Advanced Light Source. Sample surfaces of Yb{sub 14}MnSb{sub 11} and Yb{sub 14}ZnSb{sub 11} were measured as received, after Ar{sup +} ion bombardment, and after cleaving in situ. Detailed analysis of the clean Mn and Zn analog sample surfaces reveal a significant contribution of both Yb{sup 3+} and Yb{sup 2+} 4f states in the valence band region for the Zn analog and no contribution of Yb{sup 3+} states to the valence band for the Mn analog. This result is predicted for the Zn analog by Zintl counting rules, and single crystal X-ray diffraction studies presented here also support the mixed valency of Yb for Yb{sub 14}ZnSb{sub 11}. Further detailed analysis of the core and valence band structure of both Yb{sub 14}MnSb{sub 11} and Yb{sub 14}ZnSb{sub 11} will be presented.
- Research Organization:
- Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 15009723
- Report Number(s):
- UCRL-TR-200644; TRN: US0406599
- Resource Relation:
- Other Information: PBD: 2 Oct 2003
- Country of Publication:
- United States
- Language:
- English
Similar Records
Intermediate Yb valence in the Zintl phases Yb14MSb11(M=Zn,Mn,Mg): XANES, magnetism, and heat capacity
Synthesis, crystal structures, and physical properties of the new Zintl phases A{sub 21}Zn{sub 4}Pn{sub 18} (A=Ca, Eu; Pn=As, Sb)—Versatile arrangements of [ZnPn{sub 4}] tetrahedra