Mapping Phase Transformations in the Heat-Affected-Zone of Carbon Manganese Steel Welds using Spatially Resolved X-Ray Diffraction
Conference
·
OSTI ID:15005690
Spatially Resolved X-Ray Diffraction (SRXRD) was used to investigate phase transformations that occur in the heat affected zone (HAZ) of gas tungsten arc (GTA) welds in AISI 1005 carbon-manganese steel. In situ SRXRD experiments performed at the Stanford Synchrotron Radiation Laboratory (SSRL) probed the phases present in the HAZ during welding, and these real-time observations of the HAZ phases were used to construct a map of the phase transformations occurring in the HAZ. This map identified 5 principal phase regions between the liquid weld pool and the unaffected base metal. Regions of annealing, recrystallization, partial transformation and complete transformation to {alpha}-Fe, {gamma}-Fe, and {delta}-Fe phases were identified using SRXRD, and the experimental results were combined with a heat flow model of the weld and thermodynamic calculations to compare these results with the important phase transformation isotherms. From the resulting phase transformation map, the kinetics of phase transformations that occur under the highly non-isothermal heating and cooling cycles produced during welding of steels can be better understood and modeled.
- Research Organization:
- Lawrence Livermore National Lab., CA (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 15005690
- Report Number(s):
- UCRL-JC-146627-REV-1
- Country of Publication:
- United States
- Language:
- English
Similar Records
Mapping Phase Transformations in the Heat-Affected-Zone of Carbon Manganese Steel Welds using Spatially Resolved X-Ray Diffraction
Spatially resolved X-ray diffraction phase mapping and {alpha} {r_arrow} {beta} {r_arrow} {alpha} transformation kinetics in the heat-affected zone of commercially pure titanium arc welds
Direct Observation of Phase Transformations in Austenitic Stainless Steel Welds Using In-situ Spatially Resolved and Time-resolved X-ray Diffraction
Conference
·
Mon Dec 03 23:00:00 EST 2001
·
OSTI ID:15004796
Spatially resolved X-ray diffraction phase mapping and {alpha} {r_arrow} {beta} {r_arrow} {alpha} transformation kinetics in the heat-affected zone of commercially pure titanium arc welds
Journal Article
·
Sat Oct 31 23:00:00 EST 1998
· Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science
·
OSTI ID:290260
Direct Observation of Phase Transformations in Austenitic Stainless Steel Welds Using In-situ Spatially Resolved and Time-resolved X-ray Diffraction
Conference
·
Thu Sep 23 00:00:00 EDT 1999
·
OSTI ID:791505