The Effect of Welding on the Breakdown and Repassivation Potentials of Alloy 22 in 5M CaC12
Conference
·
OSTI ID:15004667
The study of the electrochemical behavior of wrought and welded Alloy 22 was carried out in 5 M CaCl{sub 2} between 45 and 120 C with Multiple Crevice Assembly (MCA) specimens. The susceptibility to corrosion was found to increase with increase in temperature in both the wrought and the welded forms of the alloy. The weld metal was found to be less susceptible to localized corrosion under the conditions tested.
- Research Organization:
- Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- W-7405-ENG-48
- OSTI ID:
- 15004667
- Report Number(s):
- UCRL-JC-155209; TRN: US0304921
- Resource Relation:
- Conference: 204th Meeting of the Electrochemical Society, Orlando, FL (US), 10/12/2003--10/16/2003; Other Information: PDF-FILE: 15 ; SIZE: 0.6 MBYTES; PBD: 28 Aug 2003
- Country of Publication:
- United States
- Language:
- English
Similar Records
A Comparison of the Effect of Temperature on the Passivity Breakdown and Repassivation Potentials of Wrought and Welded Alloy 22 in 5 M CaC12
The Effect of Temperature on the Breakdown and Repassivation Potentials of Welded Alloy 22 In 5 M CACI2
A Comparison of the Effect of Temperature on the Passivity Breakdown and Repassivation Potentials of Wrought and Welded Alloy 22 in 5 M CAC12
Conference
·
Mon Aug 11 00:00:00 EDT 2003
·
OSTI ID:15004667
The Effect of Temperature on the Breakdown and Repassivation Potentials of Welded Alloy 22 In 5 M CACI2
Technical Report
·
Wed Jul 05 00:00:00 EDT 2006
·
OSTI ID:15004667
A Comparison of the Effect of Temperature on the Passivity Breakdown and Repassivation Potentials of Wrought and Welded Alloy 22 in 5 M CAC12
Conference
·
Fri Feb 14 00:00:00 EST 2003
·
OSTI ID:15004667