Subtle and reversible interactions of ambient pressure H2 with Pt/Cu(111) single-atom alloy surfaces
- Brookhaven National Lab. (BNL), Upton, NY (United States). National Synchrotron Light Source II (NSLS-II)
- Brookhaven National Lab. (BNL), Upton, NY (United States)
Pt-Cu single-atom alloys (SAA) have been identified as promising hydrogenation catalysts with an ability to activate H2 better than the individual metals alone. We studied the interaction between H2 and Pt/Cu(111) SAA model surface using ambient pressure X-ray photoelectron spectroscopy (AP-XPS). A binding energy shift in the Pt 4f spectrum indicates the presence of adsorbed H at 350 K, occurring because of HeH bond activation. No evidence was found of either surface segregation, subsurface diffusion of Pt atoms, or any effects on the thermal stability of the surface, likely due to the subtle interaction between Pt and H. This shift is reversible upon evacuation of H2, which is a sign of a weak interaction. In addition, we studied the effect of H2 and CO coadsorption and found that while the surface is unaffected by poisoning by a small amount of CO at 350 K, CO can displace adsorbed H on almost half of the surface Pt sites at 300 K. The susceptibility to CO poisoning increases after the surface was heated to 450 K due to changes in the structure of the subsurface layer that enhance the binding of CO to the surface Pt sites.
- Research Organization:
- Brookhaven National Lab. (BNL), Upton, NY (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- Grant/Contract Number:
- SC0012704
- OSTI ID:
- 1492775
- Report Number(s):
- BNL-210926-2019-JAAM
- Journal Information:
- Surface Science, Vol. 679, Issue C; ISSN 0039-6028
- Publisher:
- ElsevierCopyright Statement
- Country of Publication:
- United States
- Language:
- English
Web of Science
Similar Records
In situ ambient pressure XPS study of Pt/Cu(111) single-atom alloy in catalytically relevant reaction conditions
Carbon Monoxide Mediated Hydrogen Release from PtCu Single-Atom Alloys: The Punctured Molecular Cork Effect