Deformation mechanisms and work-hardening behavior of transformation-induced plasticity high entropy alloys by in -situ neutron diffraction
Journal Article
·
· Materials Research Letters
- Neutron Scattering Division, Oak Ridge National Laboratory, Oak Ridge, TN, USA, School of Chemical Engineering and Technology, Tianjin University, Tianjin, People’s Republic of China
- Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, TN, USA
- Neutron Scattering Division, Oak Ridge National Laboratory, Oak Ridge, TN, USA
- Neutron Scattering Division, Oak Ridge National Laboratory, Oak Ridge, TN, USA, Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, TN, USA, Department of Materials Science and Engineering, The University of Tennessee, Knoxville, TN, USA
- Neutron Scattering Division, Oak Ridge National Laboratory, Oak Ridge, TN, USA, Department of Materials Science and Engineering, The University of Tennessee, Knoxville, TN, USA
- Sponsoring Organization:
- USDOE
- Grant/Contract Number:
- AC05-00OR22725
- OSTI ID:
- 1483317
- Journal Information:
- Materials Research Letters, Journal Name: Materials Research Letters Vol. 6 Journal Issue: 11; ISSN 2166-3831
- Publisher:
- Informa UK LimitedCopyright Statement
- Country of Publication:
- United Kingdom
- Language:
- English
Cited by: 26 works
Citation information provided by
Web of Science
Web of Science
Similar Records
Correlating work hardening with co-activation of stacking fault strengthening and transformation in a high entropy alloy using in-situ neutron diffraction
In situ neutron diffraction study of deformation behavior of a multi-component high-entropy alloy
In situ neutron diffraction study on tensile deformation behavior of carbon-strengthened CoCrFeMnNi high-entropy alloys at room and elevated temperatures
Journal Article
·
Thu Dec 17 00:00:00 EST 2020
· Scientific Reports
·
OSTI ID:1483317
+5 more
In situ neutron diffraction study of deformation behavior of a multi-component high-entropy alloy
Journal Article
·
Wed Jan 01 00:00:00 EST 2014
· Applied Physics Letters
·
OSTI ID:1483317
+5 more
In situ neutron diffraction study on tensile deformation behavior of carbon-strengthened CoCrFeMnNi high-entropy alloys at room and elevated temperatures
Journal Article
·
Fri Jun 22 00:00:00 EDT 2018
· Journal of Materials Research
·
OSTI ID:1483317
+1 more