Stabilization of Hexaaminobenzene in a 2D Conductive Metal–Organic Framework for High Power Sodium Storage
- Berzelii Centre EXSELENT on Porous Materials, Department of Materials and Environmental Chemistry, Stockholm University, Stockholm SE-106 91, Sweden
- X-ray Science Division, Advanced Photon Source, Argonne National Laboratory, Argonne, Illinois 60439, United States
Redox-active organic materials have gained growing attention as electrodes of rechargeable batteries. However, their key limitations are the low electronic conductivity and limited chemical and structural stability under redox conditions. Herein, we report a new cobalt-based ;2D conductive metal-organic framework (MOF), Co-HAB, having stable, accessible, dense active sites for high-power energy storage device through conjugative coordination between a redox-active linker, hexaaminobenzene (HAB), and a Co(II) center. Given the exceptional capability of Co-HAB for stabilizing reactive HAB, a reversible three-electron redox reaction per HAB was successfully demonstrated for the first time, thereby presenting a promising new electrode material for sodium-ion storage. Specifically, through synthetic tunability of Co-HAB, the bulk electrical conductivity of 1.57 S cm(-1) was achieved, enabling an extremely high rate capability, delivering 214 mAh g(-1) within 7 min or 152 mAh g(-1) in 45 s. Meanwhile, an almost linear increase of the areal capacity upon increasing active mass loading up to 9.6 mg cm(-2) was obtained, demonstrating 2.6 mAh cm(-2) with a trace amount of conducting agent.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- DOE Contract Number:
- AC02-06CH11357
- OSTI ID:
- 1481204
- Journal Information:
- Journal of the American Chemical Society, Vol. 140, Issue 32; ISSN 0002-7863
- Publisher:
- American Chemical Society (ACS)
- Country of Publication:
- United States
- Language:
- English