Aggregation and data analysis of corrosion studies in molten chloride and fluoride salts
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
Corrosion studies in molten fluoride and chloride salts were surveyed, and key data were aggregated into a single dataset. Studies were graphed by salt purity, temperature, sample material, container material, and experimental method (loop, capsule, crucible). To elucidate and quantify the factors that affect corrosion in molten salts, a data analysis using a newly-defined corrosion resistance score and a correlation analysis using techniques borrowed from machine learning were performed. It is shown that salt purity had the strongest correlation with corrosion rates in molten chlorides and fluorides. As a result, data analysis across varied works was inconsistent due to the lack of standardization among molten salt corrosion studies.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE
- Grant/Contract Number:
- AC05-00OR22725
- OSTI ID:
- 1479786
- Alternate ID(s):
- OSTI ID: 1703232
- Journal Information:
- Journal of Nuclear Materials, Vol. 511, Issue C; ISSN 0022-3115
- Publisher:
- ElsevierCopyright Statement
- Country of Publication:
- United States
- Language:
- English
Web of Science
Re‐establishing the paradigm for evaluating halide salt compatibility to study commercial chloride salts at 600°C–800°C
|
journal | April 2019 |
Enabling chloride salts for thermal energy storage: implications of salt purity
|
journal | January 2019 |
Similar Records
Corrosion of Candidate Materials in Molten FLiBe Salt for Fluoride-Salt-Cooled High-Temperature Reactor (FHR)
Corrosion-induced microstructural developments in 316 stainless steel during exposure to molten Li2BeF4(FLiBe) salt