Diamond and diamondlike carbon as wear-resistant, self-lubricating coatings for silicon nitride
Conference
·
OSTI ID:147157
Recent work on the friction and wear properties of as-deposited fine-grain diamond, polished coarse-grain diamond, and as-deposited diamondlike carbon (DLC) films in humid air at a relative humidity of approximately 40 percent and in dry nitrogen is reviewed. Two types of chemical vapor deposition (CVD) processes are used to deposit diamond films on silicon nitride (Si3N4) substrates: microwave-plasma and hot-filament. Ion beams are used to deposit DLC films on Si3N4 substrates. The diamond and DLC films in sliding contact with hemispherical bare Si3N4 pins have low steady-state coefficients of friction (less than 0.2) and low wear rates (less than 10(exp {minus}7) mm(exp 2)/N-m), and thus, can be used effectively as wear-resistant, self-lubricating coatings for Si3N4 in the aforementioned two environments.
- Research Organization:
- National Aeronautics and Space Administration, Cleveland, OH (United States). Lewis Research Center
- OSTI ID:
- 147157
- Report Number(s):
- N--96-13389; NASA-TM--106974; E--9735; NAS--1.15:106974; CONF-951054--; CNN: RTOP 505-63-5A
- Country of Publication:
- United States
- Language:
- English
Similar Records
Wear-resistant, self-lubricating surfaces of diamond coatings
Friction and wear properties of as-deposited and carbon ion-implanted diamond films
Wear-resistant, self-lubricating surfaces on diamond coatings
Conference
·
Mon May 01 00:00:00 EDT 1995
·
OSTI ID:63476
Friction and wear properties of as-deposited and carbon ion-implanted diamond films
Conference
·
Mon Jan 31 23:00:00 EST 1994
·
OSTI ID:36448
Wear-resistant, self-lubricating surfaces on diamond coatings
Conference
·
Sat Dec 30 23:00:00 EST 1995
·
OSTI ID:230102