Direct measurement of energy loss due to aging effects in the condensed phase explosive PBX 9404
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
The explosive performance of PBX 9404, a condensed phase explosive with HMX and nitrocellulose reactive ingredients, was evaluated using the detonation cylinder expansion test after it had been naturally aged for over 46 years. Nitrocellulose is known to chemically degrade with age, but the corresponding effect on explosive performance is currently unknown. Two new cylinder tests were fielded with the oldest known PBX 9404 explosive (>46 years) and the data was compared with prior PBX 9404 cylinder test data. A method for comparing wall motion data collected by streak camera and laser interferometry diagnostics was also introduced. Analysis of the cylinder motion indicated that the aged explosive exhibits decreased performance, which varied with cylinder expansion radius and product specific volume. This energy decrement was found to be 0.8% of the total initial explosive energy per decade of age at a product volume of 7.0 cc/g. In conclusion, the measured energy decrement in explosives older than 37 years exceeds the chemical energy content of nitrocellulose, indicating that nitrocellulose decomposition radicals are likely degrading the normally stable HMX molecules during the aging process.
- Research Organization:
- Los Alamos National Laboratory (LANL), Los Alamos, NM (United States)
- Sponsoring Organization:
- USDOE
- Grant/Contract Number:
- AC52-06NA25396
- OSTI ID:
- 1471355
- Report Number(s):
- LA-UR--17-30738
- Journal Information:
- Proceedings of the Combustion Institute, Journal Name: Proceedings of the Combustion Institute Journal Issue: 3 Vol. 37; ISSN 1540-7489
- Publisher:
- ElsevierCopyright Statement
- Country of Publication:
- United States
- Language:
- English
Similar Records
Aspects of the Tribology of the Plastic Bonded Explosive (PBX) 9404
Analysis of historical and recent PBX 9404 cylinder tests using FLAG