MIS High-Purity Plutonium Oxide Metal Oxidation Product BLO-39-11-14-004 (SSR132 and 132A): Final Report
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
A high-purity, reactor-grade plutonium dioxide material from the Material Identification and Surveillance (MIS) Program inventory has been studied with regard to gas generation and corrosion in a storage environment. BLO-39-11-14-004 is a high specific power oxide that represents Hanford process plutonium oxides from oxalate process product, oxalate precipitation of impure plutonium and pure mixed uranium/plutonium nitrate solutions, PFP NDA and impure and scrap plutonium oxides 80-85% from PFP and the 300 area. It also represents plutonium oxides from oxalate precipitation at LANL and Savannah River. After calcination to 950 °C, the material contained 80% plutonium and 7% americium with no major impurities. This study followed over time the gas pressure of a sample with nominally 0.5 wt% water in a sealed container with an internal volume scaled to 1/500th of the volume of a 3013 container. A leak occurred in the original reactor (SSR132) which was terminated after 3 years. The sample was reloaded (SSR132A) and an additional set of data was collected. Results from both loadings are discussed. Gas compositions were measured periodically over three (SSR132) and four and a half (SSR132A) year periods. The maximum observed gas pressures were 93 kPa and 94 kPa, respectively. The increase over the initial pressure was primarily due to generation of nitrogen gas. For SSR132, the maximum observed gas pressure for hydrogen was 1.2 kPa and oxygen was 9.3 kPa (includes oxygen from leak). For SSR132A, the maximum observed gas pressure for hydrogen was 5.5 kPa and oxygen was 0.9 kPa. At the completion of the study, the internal components of the sealed container showed limited signs of corrosion.
- Research Organization:
- Los Alamos National Laboratory (LANL), Los Alamos, NM (United States)
- Sponsoring Organization:
- USDOE Office of Environmental Management (EM)
- DOE Contract Number:
- AC52-06NA25396
- OSTI ID:
- 1461382
- Report Number(s):
- LA-UR-18-26650; TRN: US1901754
- Country of Publication:
- United States
- Language:
- English
Similar Records
MIS High-Purity Plutonium/Uranium Oxide Hydride Product 5501407 (SSR129): Final Report
MIS High-Purity Uranium/Plutonium Oxide Metal Oxidation Product SCP711-56 (SSR135): Final Report