Preparation and dielectric analysis of microphase-separated poly(acrylonitrile-co-acrylamide-co-acrylic acid) hydrogels
- National Taiwan Institute of Technology (Taiwan, Province of China)
The acidic hydrolysis of polyacrylonitrile was carried out to yield a variety of terpolymers made up of nitriles, amides and acids. The formation of block structure was shown to follow a ripper mechanism occurring to acrylamide groups, that is more pronounced for a certain range of acrylamide content, evidenced by the composition analysis using {sup 1}H-NMR and base titration. The rates of formation of acrylamide fraction and acid fraction in the consecutive mode are approximately the same, yielding the content of ionic groups from 0.8 to 2.2. mole percent, dependent on the time of hydrolysis. The dielectric relaxation measurement on swollen gels shows three relaxation transitions, {alpha}, {beta}, {gamma}, over -150{degrees}C to 0{degrees}C, as influenced by the chemical composition and water absorption. The {beta} and {gamma} are associated with the polymer-water interaction and short-range motion of polymers and water.
- OSTI ID:
- 141708
- Report Number(s):
- CONF-930304--
- Country of Publication:
- United States
- Language:
- English
Similar Records
Recovery of petroleum by flooding with viscous aqueous solutions of acrylic acid--acrylamide-diacetone acrylamide copolymer
The effect of acrylic comonomers on the hydrolytic stability of polyacrylamides at high temperature in alkaline solution